- Engineered Cloth–Inserted (CI) Sheet Rubber
- Performance Cloth–Inserted (CI) Sheet Rubber
Cloth–Inserted (CI) Sheet Rubber Products
Jump to Navigation
Engineered Cloth–Inserted (CI) Sheet Rubber
Cloth-Inserted (CI) Neoprene Sheet
A blended Neoprene compound with one or more polyester fabric plies, for service where dimensional stability is required. Suitable for use where moderate oil resistance is required and where hot and cold water and gases are being conveyed. Fabric content per thickness is one ply for 1/32” and 1/16”, two plies for 1/8”, three plies for 3/16”, and four plies for 1/4”.
Finish: Smooth
| Durometer Hardness Shore A ± 5 |
Thickness (Inches) |
Width (Inches) |
Tensile PSI |
Ultimate Elongation Percent |
Fabric Weight |
Fabric Type |
Temperature Range |
Estimated Weight Per Linear Foot (1/8" x 36") |
Oil Resistance |
Specifications |
|---|---|---|---|---|---|---|---|---|---|---|
| 70† | 1/16 - 1/4 | 36, 48 | 1,000 | n/a | 4 oz | Cotton or Polyester |
-30°F to +200°F |
2.5 lb | Good | ASTM D 2000 2AA 710 A13 |
*Physicals presented are typical values.
† Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
GAUGES: This construction includes one ply for each 1/16” thickness:
1/16 - 3/32 = 1 ply; 1/8” = 2 plies; 3/16” = 3 plies; 1/4” = 4 plies
HHP-151F Cloth Inserted (CI) Sheet
Designed for ventilating systems and for flange joints for water or brine systems to withstand 250 pounds of pressure. A typical application is a flange gasket in which the compression loads are so high that non-reinforced rubber would squeeze or extrude out between the flanges.
Finish: Smooth
| Class | Durometer Hardness Shore A ± 5 |
Thickness (Inches) |
Width (Inches) |
Tensile PSI |
Ultimate Elongation Percent |
Fabric Weight |
Polymer | Temperature Range |
Estimated Weight Per Linear Foot (1/8" x 36") |
Oil Resistance |
|---|---|---|---|---|---|---|---|---|---|---|
| 1 | 50 | 1/16 - 1/4 | 36, 48 | 3200 | 450 | 10.8 oz per sq yd |
SBR | -40°F to +200°F |
2.7 lb | N/A |
| 2 | 60 | 1/16 - 1/4 | 36, 48 | 1650 | 350 | 10.8 oz per sq yd |
Neoprene | -40°F to +200°F |
3.2 lb | Medium |
| 3 | 50 | 1/16 - 1/4 | 36, 48 | 1800 | 450 | 10.8 oz per sq yd |
SBR | -40°F to +200°F |
2.7 lb | N/A |
| 4 | 50 | 1/16 - 1/4 | 36, 48 | 1600 | 600 | 10.8 oz per sq yd |
NBR | -40°F to +200°F |
2.9 lb | High |
Each sheet has a ply of 10.8 oz./sq. yd. per each 1/16” gauge.
GAUGES: This construction includes one ply for each 1/16” thickness:
1/16” = 1 ply; 1/8” = 2 ply; 3/16” = 3 ply; 1/4” = 4 ply
*Physicals presented are typical values.
Performance Cloth–Inserted (CI) Sheet Rubber
Regular Ply Cloth-Inserted (CI) SBR Sheet
Cloth reinforcement enhances dimensional stability in flanged gasket applications with high compression loads. Suitable for use in air, hot water, low pressure steam, and hydraulic services. An SBR compound reinforced with a close weave polyester or cotton fabric. This construction includes one ply of fabric for each 1/16” thickness.
Finish: Smooth
| Durometer Hardness Shore A ± 5 |
Thickness (Inches) |
Width (Inches) |
Tensile PSI |
Ultimate Elongation Percent |
Fabric Weight |
Fabric Type |
Temperature Range |
Estimated Weight Per Linear Foot (1/8" x 36") |
Oil Resistance |
Specifications |
|---|---|---|---|---|---|---|---|---|---|---|
| 65 | 1/16 - 1/4 | 36, 48 | 900 | 200 | 4.0 oz | Cotton or Polyester |
-20°F to +170°F |
3.9 lb | None | ASTM D 2000 1AA 609 |
*Physicals presented are typical values.
Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
GAUGES: This construction includes one ply for each 1/16” thickness:
1/16 - 3/32 = 1 ply; 1/8” = 2 plies; 3/16” = 3 plies; 1/4” = 4 plies
Reduced Ply Cloth-Inserted (CI) SBR Sheet
Like Regular Ply CI sheet, Reduced Ply CI sheet addresses the need for dimensional stability in applications with high compression loads. Fabric content per thickness is one ply for 1/8”, two plies for 3/16”, and three plies for 1/4”.
Finish: Smooth
| Durometer Hardness Shore A ± 5 |
Thickness (Inches) |
Width (Inches) |
Tensile PSI |
Ultimate Elongation Percent |
Fabric Weight |
Fabric Type |
Temperature Range |
Estimated Weight Per Linear Foot (1/8" x 36") |
Oil Resistance |
Specifications |
|---|---|---|---|---|---|---|---|---|---|---|
| 65 | 1/8 - 1/4 | 48, 72 | 900 | 200 | 4.0 oz | Cotton or Polyester |
-20°F to +170°F |
4.1 lb | None | ASTM D 2000 1AA 609 |
*Physicals presented are typical values.
Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
GAUGES: This construction includes one ply for each 1/16” thickness:
1/8" = 1 ply; 3/16” = 2 plies; 1/4” = 3 plies