Cloth reinforcement enhances dimensional stability in flanged gasket applications with high compression loads. Suitable for use in air, hot water, low pressure steam and hydraulic services. Available in a variety of elastomers: SBR, Neoprene and Nitrile. Good rsistance to alkalis and acids. |
| |
|
| |
|
| |
|
| |
ENGINEERED CLOTH INSERTED (CI) SHEET RUBBER:
|
| |
Cloth Inserted (CI) Neoprene |
A blended Neoprene compound with one or more polyester fabric plies, for service where dimensional stability is required. Suitable for use where moderate oil resistance is required and where hot and cold water and gases are being conveyed. Fabric content per thickness is one ply for 1/32” and 1/16”, two plies for 1/8”, three plies for 3/16”,
and four plies for 1/4”. |
Temperature Range: -20°F to +180°F Finish: Smooth |
Durometer
Hardness
Shore ± 5 |
Thickness
(Inches) |
Width
(Inches) |
Tensile
PSI |
Ultimate
Elongation
Percent |
Fabric
Weight |
Fabric
Type |
Estimated Weight
Per Linear Foot
(1/8" x 36") |
Oil
Resistance |
Specifications |
70 |
1/32 - 1/4 |
48 |
600 |
250 |
4.0 oz |
Cotton
or
Polyester |
4.0 lb |
Good |
ASTM D 2000
1BC 706 |
|
|
Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
This construction includes one ply for each 1/16” thickness: 1/16 - 3/32 = 1 ply 1/8” = 2 plies 3/16” = 3 plies 1/4” = 4 plies |
HH-P-151F Cloth Inserted (CI) Sheet |
Designed for ventilating systems and for flange joints for water or brine systems to withstand 250 pounds of pressure. A typical application is a flange gasket in which the compression loads are so high that non-reinforced rubber would squeeze or extrude out between the flanges. |
Fabric Weight: 10.8 oz per sq. yd Finish: Smooth and Fabric |
Class |
Durometer
Hardness
Shore ± 5 |
Thickness
(Inches) |
Width
(Inches) |
Tensile*
PSI |
Ultimate
Elongation*
Percent |
Polymer |
Temperature |
Estimated Weight
Per Linear Foot
(1/8" x 36") |
Oil
Resistance |
1 |
50 |
1/16 - 1/4 |
36, 48 |
1800 |
450 |
SBR |
-40°F
to +200°F |
|
N/A |
2 |
60 |
1/16 - 1/4 |
36, 48 |
1650 |
350 |
Neoprene |
-40°F
to +220°F |
3.2 lb |
Medium |
3 |
50 |
1/16 - 1/4 |
36, 48 |
1800 |
450 |
SBR |
-40°F
to +200°F |
2.7 lb |
N/A |
4 |
50 |
1/16 - 1/4 |
36, 48 |
1600 |
600 |
Nitrile |
-40°F
to +250°F |
2.9 lb |
High |
|
|
Each sheet has a ply of 10.8 oz./sq. yd. per each 1/16” gauge.
GAUGES: This construction includes one ply for each 1/16” thickness (1/16” = 1 ply, 1/8” = 2 ply, 3/16” = 3 ply, 1/4” = 4 ply)
*Typical Values
|
|
| |
PERFORMANCE CLOTH INSERTED (CI) SHEET RUBBER:
|
| |
Regular Ply Cloth Inserted (CI) SBR Sheet |
Cloth reinforcement enhances dimensional stability in flanged gasket applications with high compression loads. Suitable for use in air, hot water, low pressure steam, and hydraulic services. An SBR compound reinforced with a close weave polyester or cotton fabric. This construction includes one ply of fabric for each 1/16” thickness. |
Temperature: -20°F to +170°F Finish: Smooth |
Durometer
Hardness
Shore ± 5 |
Thickness
(Inches) |
Width
(Inches) |
Tensile
PSI |
Ultimate
Elongation
Percent |
Fabric
Weight |
Fabric
Type |
Estimated Weight
Per Linear Foot
(1/8" x 36") |
Oil Resistance |
Specifications |
65 |
1/16 - 1/4 |
36, 48 |
900 |
200 |
4.0 oz |
Cotton
or
Polyester |
3.9 lb |
None |
ASTM D 2000
1AA 609 |
|
|
Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
This construction includes one ply for each 1/16” thickness: 1/16 - 3/32 = 1 ply; 1/8” = 2 plies; 3/16” = 3 plies; 1/4” = 4 plies
|
Reduced Ply Cloth Inserted (CI) SBR Sheet |
Like Style 48, reduced ply CI sheet addresses the need for dimensional stability in applications with high compression loads. Fabric content per thickness is one ply for 1/8”, two plies for 3/16”, and three plies for 1/4”. |
Temperature: -20°F to +170°F Finish: Smooth |
Durometer
Hardness
Shore ± 5 |
Thickness
(Inches) |
Width
(Inches) |
Tensile*
PSI |
Ultimate
Elongation*
Percent |
Fabric
Weight |
Fabric
Type |
Estimated Weight
Per Linear Foot
(1/8" x 36") |
Oil Resistance |
Specifications |
65 |
1/8 - 1/4 |
48, 72 |
900 |
200 |
4.0 oz |
Cotton
or
Polyester |
4.1 lb |
None |
ASTM D 2000
1AA 609 |
|
|
Durometer and tensile strength of the above material is calculated with the respective material inserted into the sheet.
This construction includes one ply for each 1/16” thickness: 1/8" = 1 ply; 3/16” = 2 plies; 1/4” = 3 plies
|
|
| |
|
|
| |
|
|
| |
|
|
|
| |
|
|
|
|
|
WEST AMERICAN RUBBER COMPANY, LLC | 1413 BRADEN COURT · ORANGE, CALIFORNIA 92868 | TEL: 714-532-3355 | sales@warco.com
BILTRITE RIPLEY OPERATIONS, LLC | P.O. Box 577 · RIPLEY, MISSISSIPPI | TEL: 800-245-8748 | biltritesales@warco.com |
An ISO 9001:2000 Certified Company
WARCO and BILTRITE logos and slogan are ® registered trademarks of West American Rubber Company, LLC
Contents © 2007 West American Rubber Company, LLC
|